Studi Pengaruh Perlakuan KOH Terhadap Kekuatan Tarik Komposit Serat Rami
-
Putra E. Lado(1)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
-
Dominggus G. H. Adoe(2)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
-
Jack C.A. Pah(3*)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
(*) Corresponding Author
Abstract
Currently, natural fiber composites have become the main choice for several industrial applications in the world. The strength of natural fibers such as hemp is based on laboratory results of mechanical strength testing which show that hemp has very suitable properties as a reinforcing composite for prosthetic socket materials. The tensile test is a mechanical stress-strain test that aims to determine the strength of a material against tensile forces. In the test, the test material is pulled until it breaks. Tensile testing is carried out to look for stress and strain (stress-strain test). From this test, we can know some of the mechanical properties of materials that are needed in engineering design. The results of research conducted on the study of the effect of KOH treatment on the tensile strength of hemp fiber composites show three things. First, the highest tensile stress value in hemp fiber was found in the 2% KOH treatment with a long soaking time of 2 hours with a value of 25.3 MPa. Second, the lowest tensile strain value in hemp fiber was found in the 6% KOH treatment with a long soaking time of 2 hours with a value of 0.1%. Third, the highest modulus of elasticity in hemp fiber was found in 6% KOH treatment with a 1-hour soaking time with a value of 47.1 MPa
Downloads
References
[2]. Handoyo, m. A. (2019). Bab ii tinjauan pustaka bab ii tinjauan pustaka 2.1. 1–64. Gastronomía ecuatoriana y turismo local., 1(69), 5–24.
[3]. Mardiyanto. (2008). Analisa pengujian tarik pipa komposit serat batang pisang bermatrik polyester bqtn 157 dengan sudut serat 650/-650 pada variasi temperatur ruang uji. Ilusi senja, 31.
[4]. Marsyahyo, e., jamasri, rochardjo, h. S. B., & soekrisno. (2009). Preliminary investigation on bulletproof panels made from ramie fiber reinforced composites for nij level ii, iia, and iv. Journal of industrial textiles, 39(1), 13–26. Https://doi.org/10.1177/1528083708098913.
[5]. Maulana, i. (2021). Pengaruh lama perendaman larutan koh terhadap kekuatan tarik dan kekuatan bending komposit hibrid serat rami dan bambu. Jurnal teknik mesin, 09(03), 99–104.
[6]. Peijs, t. (2002). Composites turn green. E-polymers. Department of materials, queen mary, university of london, 1–12. Https://scholar.google.co.uk/scholar?hl=en&q=peijs%2c+t.+%282002%29+%27composites+turn+green.+e-polymers%27%2c+t_002+department+of+materials%2c+queen+mary%2c+university+of+london%2c+pp.+1-12.&btng=&as_sdt=1%2c5&as_sdtp=#0
[7]. Perlakuan, p., koh, l., tarik, k., serat, k., batang, k., mesin, t., teknik, k., brawijaya, u., & teknik, f. (2018). Pengaruh perlakuan larutan koh terhadap kekuatan tarik komposit serat kulit batang maja dengan epoxy.
[8]. Setiawan, d. (2017). Analisis uji rockwell dengan sifat-sifat bahan teknik. 07, 21–37.
[9]. Setyahandana, b., & hille, y. T. (2006). Pemanfaatan serat rami sebagai bahan penguat komposit. Prosiding. bkstm.org, november, 21–23. Http://prosiding.bkstm.org/prosiding/2006/m1 - 027.pdf
[10]. Wang, b., panigrahi, s., tabil, l., crerar, w., sokansanj, s., & braun, l. (2003). Modification of flax fibres by chemical treatment. Csae/scgr, 03, 6–9.
[11]. Yani, m., & lubis, f. (2018). Pembuatan dan penyelidikan perilaku mekanik komposit diperkuat serat limbah plastikakibat beban lendutan. Teknik mesin itm, 4(2), 77–84. Http://download.garuda.kemdikbud.go.id/article.php?article=1279382&val=17049&title=pembuatan dan penyelidikan perilaku mekanik komposit diperkuat serat limbah plastik akibat beban lendutan.