PENGARUH WAKTU DAN TEMPERATUR HIDROTERMAL TERHADAP HASIL UJI XRD HIDROKSIAPATIT DARI CANGKANG KERANG ALE-ALE
-
AGUSTO BRIA SERAN(1*)
TEKNIK MESIN FAKULTAS SAINS DAN TEKNIK UNIVERSITAS NUSA CENDANA
-
Erich U. K. Maliwemu(2)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
-
Dominggus G. H. Adoe(3)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
(*) Corresponding Author
Abstract
This study aims to analyze the changes in chemical composition and phase of ale-ale shells through X-Ray Diffraction (XRD) tests with variations in temperature and oven time. Ale-ale shell samples obtained from Oesapa Beach, Kupang, East Nusa Tenggara, were processed through the preparation, heating, and characterization stages using XRD. Testing was carried out at temperatures of 500°C and 700°C with variations in heating time of 2, 4, and 6 hours. The results of the XRD test showed phase changes in samples heated at a temperature of 500°C, where in samples with a time of 6 hours decomposition occurred into CaO with a purity level of 53.4%. At a temperature of 700°C, samples heated for 2 hours showed a purity of 53.3%, and at 6 hours the purity reached 48.2%. All samples showed diffraction peaks indicating 100% calcite content. These results provide an understanding of the changes in the crystal structure and purity of ale-ale shell material, which can be used in biomaterial applications, especially for bone graft materials.
Downloads
References
Affandi, A., Amri, A., & Zultiniar, Z. (2015). Sintesis Hidroksiapatit Dari Cangkang Kerang Darah (Anadara granosa) dengan Proses Hidrotermal Variasi Rasio Mol Ca/P dan Suhu Sintesis (Doctoral dissertation, Riau University).
Afriadi, P. (2021). PENGARUH PELAPISAN HIDROKSIAPATIT TERHADAP LAJU KOROSI DAN BIOAKTIVITAS TI-6Al-4V ELI DALAM SIMULATED BODY FLUID (Doctoral dissertation, Universitas Andalas).
Afrizal, G. (2016). Analisa struktur mikro material substitusi hidroksiapatit cangkang kerang darah dan resin akrilik bahan pembuat gigi untuk aplikasi gigi tiruan. J Surya Tek, 2(04), 1-9.
Anggraeni, N. C. (2022). SINTESIS HIDROKSIAPATIT (HAp) DARI BATU KAPUR LAMPUNG SELATAN MENGGUNAKAN METODE PRESIPITASI.
BAHAN, K. B. S., & ULFYANA, D. SINTESIS DAN KARAKTERISASI HIDROKSIAPATIT DARI LIMBAH SISIK IKAN KAKAP MERAH (Lutjanus campechanus) MENGGUNAKAN METODE PENGENDAPAN.
Fadhilah, R., Kurniawan, R. A., & Icha, M. M. (2015). Sintesis hidroksiapatit dari cangkang kerang Ale-ale (Meretrix spp) sebagai material graft tulang. Jurnal Buletin Al-Ribaath, 12(1).
Giri, A. S. (2016). Efektivitas Ekstrak Daun Sirsak Sebagai Inhibitor Pada Baja Karbon Api 5l Dalam Larutan Nacl 3%.
Hidayati, Y. Sintesis dan Performa Active Carbon Hasil Hydrothermal Dari Kulit Cicer Arietinum (Kacang Arab) Pada Baterai Li-S (Bachelor's thesis, Fakultas Sains dan Teknologi UIN Syarif Hidayatullah Jakarta).
Lele, I. S. T., Maliwemu, E. U., & Adoe, D. G. (2022, April). KARAKTERISASI OMATERIAL HIDROKSIAPATIT DARI CANGKANG KERANG ALE-ALE PANTAI OESAPA KOTA KUPANG. In Seminar Nasional Kimia dan Pendidikan Kimia (Vol. 1, No. 1, pp. 56-62).
Mozartha, M. (2015). Hidroksiapatit dan aplikasinya di bidang kedokteran gigi. Cakradonya Dental Journal, 7(2), 835-841.
Rahmawati, E. (2023). Sintesis NiFe2O4 Dan NiFe2O4/Bentonit untuk Oksidasi Katalitik Metil Violet (Doctoral dissertation, Universitas Islam Indonesia).
Suci, I. A., & Ngapa, Y. D. (2020). Sintesis dan karakterisasi hidroksiapatit (HAp) dari cangkang kerang ale-ale menggunakan metode presipitasi double stirring. CAKRA KIMIA (Indonesian E-Journal of Applied Chemistry), 8(2), 73-81.
Sumadi, R., Deswardani, F., & Restianingsih, T. (2023). Sintesis dan Karakterisasi Membran Komposit dari Hidroksiapatit Kerang Dara-Kitosan sebagai Aplikasi Biokomposit (Doctoral dissertation, UNIVERSITAS JAMBI).
Tua, B., & Amri, A. (2016). Sintesis dan Karakterisasi Hidroksiapatit dari Cangkang Kerang Darah dengan Proses Hidrotermal Variasi Suhu dan PH (Doctoral dissertation, Riau University.
Widyastuti, S. S., & Fajarin, R. PENGARUH PERSEN MASSA POLIAMIDA-6 DAN TEMPERATUR SINTERING TERHADAP MIKROSTRUKTUR DAN SIFAT MEKANIK PROYEKTIL KOMPOSIT TEMBAGA–POLIAMIDA (Cu-PA6).
Yuliana, R., Rahim, E. A., & Hardi, J. (2017). Sintesis hidroksiapatit dari tulang sapi dengan metode basah pada berbagai waktu pengadukan dan suhu sintering. KOVALEN: Jurnal Riset Kimia, 3(3), 201-210.
Copyright (c) 2025 LONTAR Jurnal Teknik Mesin Undana
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.