Mechanical Testing of Palm Fiber Pretreatment NaOH With Polyester Matrix Material
-
Josef Etheldreda Nana(1*)
TEKNIK MESIN FAKULTAS SAINS DAN TEKNIK UNIVERSITAS NUSA CENDANA
-
Dominggus G. H. Adoe(2)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
-
Rima Nindia Selan(3)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
(*) Corresponding Author
Abstract
In this increasingly developing era, the manufacturing industry is experiencing very rapid development. The need for materials in this field is also increasing. Materials with certain characteristics such as strength, toughness, and other mechanical properties according to needs are highly sought after. Composite is a material formed from a combination of two or more constituent materials through a non-homogeneous mixture, where the mechanical properties of each constituent material are different, the use of composite materials properly and efficiently requires extensive knowledge of their mechanical properties. While the use of ijuk is still limited to household needs, even exported in raw material conditions, therefore the use of ijuk as a basic material for composites is a new hope for utilizing ijuk into a commodity that has higher added value. The results of the study on the Testing of Ijuk Fiber Mechanics Pre Treatmeat Naoh With Polyester Matrix Material concluded that concentration affects the bending strength of 9.44 N / mm2 and deflection of 37.94 mm of ijuk fiber with the best results at a concentration with a soaking time of 60 minutes.
Downloads
References
[2] Ellayawan Arbintarso, S. (2009). Tinjauan Kekuatan Lengkung Papan Serat Sabut Kelapa Sebagai Bahan Teknik. Jurnal Teknologi, 2(1), 53–60.
[3] Firdaus, M. Y. (2021). Pengujian Karakterisasi Material Komposit Berpenguat Serat Alam Fraksi Volume 10% Metode Injection Molding. 1–29.
[4] Hastomo, B. (2009). Analisis Pengaruh Sifat Mekanik Material Terhadap Distribusi Tegangan Pada Proses Deep Drawing Produk End Cup Hub Body Maker dengan Menggunakan Software Abaqus 6.5-1. Jurusan Teknik Mesin Universitas Muhammadiyah Surakarta, 28–29.
[5] Irsyad, M. (2015). Sifat Fisis dan Mekanis pada Komposit Polyester Serat Batang Pisang yang Disusun Asimetri [45/-30/45/-30]. Teknoin
[6] Mahmuda, E., Savetlana, S., & Sugiyanto, D. (2013). Pengaruh Panjang Serat Terhadap Kekuatan Tarik Komposit Berpenguat Serat Ijuk dengan Matrik Epoxy. Jurnal Ilmiah Teknik Mesin, 1(3), 79–84.
[7] Maliwemu, E. U. K., & Adoe, D. G. H. (2015). Pengaruh Perlakuan Alkali Serat Sabut Kelapa terhadap Kekuatan Tarik Komposit Polyester. Lontar Jurnal Teknik Mesin Undana (LJTMU), 2(1), 61–68. http://ejournal-fstunc.com/index.php/LJTMU
[8] Muhammad Khoiruddin. (2013). Studi Perbandingan Panjang Kritis Pada Beberapa Macam Serat Alam Dengan Metode Pull Out Fiber Test. 4–25.
[9] Mukmin, K. (2019). Pengaruh arah serat ijuk terhadap kekuatan tarik dan bending material komposit serat ijuk-epoxy.
[10] Munandar, I., Savetlana, S., & Sugiyanto, S. (2013). Kekuatan Tarik Serat Ijuk (Arenga Pinnata Merr). Jurnal Ilmiah Teknik Mesin FEMA, 1(3), 97942.
[11] Nova Iskandar, M. (2016). Modifikasi Alat Uji Bending Sistem Mekanik Hidrolik Dan Hasil Pengujian Untuk Bahan Kuningan. Politeknik Negeri Sriwijaya., 1– 64.
[12] Pell, Y. M., & Bunganaen, W. (2014). Pengaruh Perendaman NaOHLima Persenterhadap Kekuatan TarikSeratWiduri. Lontar Jurnal Teknik Mesin Undana, 01(02), 59–65.
[13] Pratama, W. D., & Hadi, S. (2019). Hubungan Antara Persentase Berat Dan Sudut Serat Terhadap Kekuatan Lentur Papan Komposit Ijuk. Elemen : Jurnal Teknik Mesin, 6(2), 121. https://doi.org/10.34128/je.v6i2.94
[14] Samlawi, A. K., Firmana Arifin, Y., & Permana, P. Y. (2018). Pembuatan Dan Karakterisasi Material Komposit Serat Ijuk (Arenga Pinnata) Sebagai Bahan Baku Cover Body Sepeda Motor Preparation and Characterization of Composite Materials of Ijuk Fiber (Arenga pinnata) as a Motorcycle Body Cover Raw Material. Prosiding Seminar Nasional Lingkungan Lahan Basah, 3(April), 380–383
[15] Setyawan, R. T., & Riyadi, S. (2020). (2020). 3763-7352-1-Sm (1). “Analisis Variasi Struktur Serat Rami Komposit Matrik Epoksi Terhadap Kekuatan Uji Balistik Dan Bending,” 16(2), 111–115.
[16] Sinaga, B. (2019). Analisa Kekuatan Tarik Komposit Yang Diperkuat Dengan Serat Pohon Aren (Ijuk) Dengan Resin Polyester Dengan Variasi Acak, Lurus, Terputus-Putus Pendek.
[17] Sinaga, B., Manurung, C. S. P., Napitupulu, R. A. M., Tampubolon, M., & Sihombing, S. (2022). Analisa Kekuatan Tarik dan Kekerasan Komposit Resin Polyester yang Diperkuat dengan Serat Pohon Aren (Ijuk) dengan Variasi Acak, Lurus dan Terputus-Putus Pendek. Citra Saind Teknologi, 1(2), 50–58.
[18] Surono, U. B., & Sukoco. (2016). Analisa sifat fisis dan mekanis komposit serat ijuk dengan bahan matrik poliester. Prosiding Seminar Nasional XI “Rekayasa Teknologi Industri Dan Informasi, 11, 298–303.
[19] Susilowati, S. E., & Saidah, A. (2019). Pelatihan Pemanfaatan Serat Alam (Sabut Kelapadan Jerami Padi) Bagi Warga Desa Jaya RaharjaKecamatan Sukajaya Kabupaten Bogor. Berdikari, 2, 35–43.
[20] Trisna, H., & Mahyudin, A. (2012). Analisis Sifat Fisis Dan Mekanik Papan Komposit Gipsum Serat Ijuk Dengan Penambahan Boraks (Dinatrium Tetraborat Decahydrate ). Jurnal Fisika Unand, 1(1), 30–36.
[21] Yasykur, A. (2020). Pembuatan Katub Buang Pompa Hidram Berbahan Serat Tandan Kosong Kelapa Sawit Untuk Diaplikasikan di Sungai Seputih Lampung Tengah. Laporan Proyek Akhir, 1–23.
Copyright (c) 2025 LONTAR Jurnal Teknik Mesin Undana
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.