HEAT TREATMENT PADA MATA PISAU ALAT PENGHANCUR ARANG BIOMASA UNTUK MENINGKATKAN NILAI KEKERASAAN DENGAN VARIASI TEMPERATUR
-
Agustinus Otu(1*)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
-
Jack C.A. Pah(2)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
-
Jahirwan Ut Jasron(3)
Program Studi Teknik Mesin, Fakultas Sains dan Teknik Universitas Nusa Cendana
(*) Corresponding Author
Abstract
. This is evidenced by the large use of steel in various machine components, work materials and building construction, both in the form of plates, sheets, pipes and so on. Damage that often occurs in the application of ST 41 steel is wear. Wear occurs due to the influence of external forces in the form of friction and is the most dominant factor in damage to the function of machinery. As a result, the service life and performance of various machine components are reduced and indirectly will increase maintenance costs. The public demand for this metal hardening technology is increasing, so researchers have tried to apply knowledge about metal hardening to knives with low carbon steel materials. Heat treatment aims to increase ductility.. This study shows that Heat Treatment with different temperatures and different cooling media can significantly affect the hardness of low carbon steel. The results of the study showed that the highest hardness of low carbon steel was obtained at a temperature of 950°C with oil cooling media, which was 44.30 HRC.
Downloads
References
Adipura, A., & Nafi, M. (2022). Analisa Pengaruh Heat Treatment Temperring Dengan Variasi Waktu Tahan Dan Media Pendingin Terhadap Sifat Mekanik Baja Karbon Rendah. In Senakama: Prosiding Seminar Nasional Karya Ilmiah Mahasiswa (Vol. 1, No. 1, pp. 203-212).
Aditia, S. L., Helmy, P., & Darmanto, D. (2021). Analisis Pengaruh Laju Korosi Terhadap Hasil Pengelasan SMAW Dengan Berbagai Media Pendingin (Doctoral dissertation, Universitas Wahid Hasyim).
Bataviandi, F. A. D., Herman Pratikno, S. T., & Hadiwidodo, Y. S. (2022) Analisis Uji Ketahanan Coating Nanosilika Dan Geopolimer Sebagai Ketahanan Panas Dan Korosi Pada Baja Astm A36.
Callister, William, Materials Science and Engineering., 7th ed., Jhon Wiley and Sons inc, 2007.
Furqon, G. R., & Firman, M. (2016). Analisa Uji Kekerasan pada Poros Baja ST 60 dengan Media Pendingin yang Berbeda. Al Jazari: Jurnal Ilmiah Teknik Mesin, 1(1).
Gunawan, A. R., Mufarida, N. A., & Finali, A. (2021) Pengaruh Variasi Temperatur Pemanas Dan Media Pendingin Terhadap Tingkat Kekerasan Baja St 42 The Effect Of Temperature And Cooling Media Variation On The Hardness Level Of St 42 Steel.
Handoyo, Y. (2015). Pengaruh quenching dan tempering pada baja jis grade S45C terhadap sifat mekanis dan struktur mikro crankshaft. Jurnal Ilmiah Teknik Mesin, 3(2), 102-115. Jordi, M., Yudo, H., & Jokosisworo, S. (2017). Analisa Pengaruh Proses Quenching Dengan Media Berbeda Terhadap Kekuatan Tarik dan Kekerasan Baja St 36 Dengan Pengelasan SMAW. Jurnal Teknik Perkapalan, 5(1).
Jordi, M., Yudo, H., & Jokosisworo, S. (2017). Analisa Pengaruh Proses Quenching Dengan Media Berbeda Terhadap Kekuatan Tarik dan Kekerasan Baja St 36 Dengan Pengelasan SMAW. Jurnal Teknik Perkapalan, 5(1).
Khakim, A. L. (2020). Pengaruh Variasi Media Pendingin Pada Sifat Mekanis Baja Karbon Rendah Untuk As Roda Sepeda Motor. Universitas Pancasakti Tegal.
Kusniawati, E., Sari, D. K., & Putri, M. K. (2023). Pemanfaatan Sekam Padi sebagai Karbon Aktif untuk Menurunkan Kadar pH, TURBIDITY, TSS, dan TDS. Journal of Innovation Research and Knowledge, 2(10), 4183-4198.
Meli, M., Lubis, G. S., & Wicaksono, R. A. (2022). Analisa Pengaruh Heat Treatment Nilai Uji Kekerasan Pada Mata Pisau Mesin Pencacah Botol Limbah Plastik. JTRAIN: Jurnal Teknologi Rekayasa Teknik Mesin, 3(2), 27 31.
Panjaitan, A. (2015). Pengaruh Bahan Baku Arang Aktif Pada Proses Carburizing Terhadap Sifat Mekanis Baja Bohler EMS-45 Untuk Center Dead Mesin Bubut Konvensional. Mekanik, 1(2), 329143.
Perdana, D. (2017). Pengaruh Variasi Temperatur Pada Proses Perlakuan Panas Baja AISI 304 Terhadap Laju Korosi. Teknika: Engineering and Sains Journal, 1(1), 67-72.
Prasetyo, W. A. (2024). Analisis Performa Pompa Sea Water Guna Menunjang Operasional Bongkar Muat Di Kapal Mt. Gunung Kemala. Institut Teknologi Sepuluh Nopember.
Ramadhan, Y. P. P. (2017). Analisis Pengaruh Variasi Waktu Tahan dan Media Pendingin Proses Hardening pada Sifat Kekerasan Baja Aisi 8655 sebagai Solusi Kegagalan pada Hammer Crusher (Doctoral dissertation, Institut Teknologi Sepuluh Nopember).
Rifnaldy, R., & Mulianti, M. (2019). Pengaruh perlakuan panas hardening dan tempering terhadap kekerasan (hardness) baja AISI 1045. Ranah Research: Journal of Multidisciplinary Research and Development, 1(4), 950-959.
Sidiq, M. F., & Wilis, G. R. (2021). Analisa Penguatan Mata Pisau Mesin Pencacah Sampah Organik Dengan Proses Heat Treatment Bertingkat. Jurnal Crankshaft, 4(1), 93-102.
Copyright (c) 2025 LONTAR Jurnal Teknik Mesin Undana
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.