Pengaruh Perlakuan Alkali (NaOh) pada Serat Agave Cantula terhadap Kekuatan Tarik Komposit Polyester
-
Jorhans J. S. Nesimnasi(1)
-
Kristomus Boimau(2)
Jurusan Teknik Mesin, Fakultas Sains dan Teknik, Universitas Nusa Cendana
-
Yeremias M. Pell(3)
Jurusan Teknik Mesin, Fakultas Sains dan Teknik, Universitas Nusa Cendana
(*) Corresponding Author
Abstract
ABSTRACT
Purpose of this research is to know the influence of alkali treatment on tensile properties of agave cantula fiber reinforced composite with polyester matrix. Fiber of agave cantula soaked in alkali solution (2% and 5% NaOH) during 2, 4 and 6 hour. After that, the fiber cleaned use water and dried naturally. Matrix which is used in this research is polyester unsaturated resin 157 BQTN with MEKPO hardener. Composite made with method press molding at Vf = 25%. The tensile testing is made related at standard of (American standard of testing materials) ASTM D-638. Tensile testing is done with universal testing machine and the elongations of measured by using meter shove. Result of this research indicate that highest tensile stress obtained on 5% alkali treatment during 2 hour with value is 36,866 Mpa while the lowest tensile stress obtained on 2% alkali treatment during 2 hour with value is 22.707 Mpa. Highest tensile strain obtained on 5% alkali treatment during 6 hour with value 2, 449% while lowest tensile strain obtained on 2% alkali treatment during 4 hour with value 1.780%. Highest Elasticity modulus obtained on 2% alkali treatment during 4 hour with value 18.078 MPa, while the lowest elasticity modulus obtained on the 2% alkali treatment during 2 hour with value 11,203 MPa.
Downloads
References
ASTM D 638, Standard Test Method for Tensile Properties of Plastic.
Bakri, dkk 2012. “Analisis Variasi Panjang Serat Terhadap Kuat Tarik Dan Lentur Pada Komposit Yang Diperkuat Serat Agave angustifolia Haw”. Jurnal Mekanika, Jurusan Teknik Mesin Universitas Tadulako, Palu
Carli, dkk. 2012, “Analisis Kekuatan Tarik Dan Lentur Komposit Serat Gelas Jenis Woven dengan Matriks Epoxy dan Polyester berlapis Simetri Dengan Metoda Manufaktur Hand Lay- Up” ,Jurusan Teknik Mesin, Politeknik Negeri Semarang, Jurusan Teknik Mesin, Universitas Diponegoro Semarang.
Diharjo.K, 2006, ”Pengaruh Perlakuan Alkali terhadap Sifat Tarik Bahan Komposit Serat Rami-Polyester”, Jurusan Teknik Mesin Fakultas TeknikUniversitas Negeri Sebelas Maret
Fitriyani R, dkk. 2012 “Analisis Pengaruh Perlakuan Serat Terhadap Kekuatan Tarik Serat Agave Cantula Roxb” Mahasiswa Program Pasca Sarjana Magister Teknik Mesin UNS
Gibson, 1994.Principle Of Composite Material Mechanics. New York : Mc Graw Hill,Inc.
Hartanto.L, 2009. “Study Perlakuan Alkali dan Fraksi Volume Serat Terhadap Kekuatan Bending Tarik dan Impak Komposit Berpenguat Serat Rami Bermatriks Polyester BQTN 157”. Universitas Muhammadiyah Surakarta.
Jamasri, 2008. “Prospek Pengembangan Komposit Serat Alam Di Indonesia”. Fakultas Teknik Universitas Gadjah Mada.
Jones, M. R., 1975, Mechanics of Composite Material, Mc Graww Hill Kogakusha, Ltd.
Nurmaulita, 2010. “Pengaruh Orientasi Serat Sabut Kelapa Dengan Resin Polyester Terhadap Karasteristik Papan Lembaran”. Uniersitas sumatra utara.
Oroh.J, dkk 2013.”Analisis Sifat Mekanik Material Komposit Dari Serat Sabut Kelapa”. Universitas Sam Ratulangi Manado
Rahman. M. B. N, dkk. 2011. “Pengaruh Fraksi Volume Serat dan Lama Perendaman Alkali terhadap Kekuatan Impak Komposit Serat Aren-Polyester”. Jurnal Ilmiah Semesta Teknika.
Sigit Hidayat Nuri, dkk 2006. ”Kajian Komprehensif Pengaruh Perlakuan Alkali
Terhadap Kekuatan Komposit Berpenguat Serat Nanas-Nanasan (Bromeliaceae)”. Jurnal Ilmiah Semesta Teknika, Vol. 9, No. 2. Teknik Mesin FT Universitas Muhammadiyah Yogyakarta, Teknik Mesin Fakultas Teknik UNS
Setyawan. P. D, dkk. 2012, “Pengaruh Orientasi Dan Fraksi Volume Serat Daun Nanas(Ananas Comosus) Terhadap Kekuatan Tarik Komposit Polyester Tak Jenuh (Up)”, Dosen Jurusan Teknik Mesin Universitas Mataram NTB, Jl. Majapahit No. 62 Mataram.
Yudo H., Jatmiko S., 2008, “Analisa Teknis Kekuatan Mekanis Material Komposit Berpenguat Serat Ampas Tebu (Baggase) Ditinjau Dari Kekuatan Tarik Dan Impak”, Universitas Diponegoro.
http://fullerena.blogspot.com/2011/04/pengertian-dan-manfaat-serat-alam.html diakses pada tanggal 18 April pukul 22:35
http:// Published. by airinkarina.com definisi Serat dan Jenis-Jenisnya diakses pada tanggal 18 April pukul 22:35
http://mytekstil.blogspot. com serat-tekstil.html diakses pada tanggal 28 pebruari pukul 11:15
http: //dodyariawan. blogspot. com serat- nanas- sabrang- potensi-bahan baku.html) diakses pada tanggal 19 januari pukul 20:14
http://adhikusumastuti.blogspot.com.potensi-serat-nanas-sabrang-sebagai.html. diakses pada tanggal 19 januari pukul 20:14