Pengaruh Temperatur Pengovenan terhadap Sifat Mekanik Komposit Hibrid Polyester Berpenguat Serat Glass dan Serat Daun Gewang
-
Adoniram Sabuin(1)
-
Kristomus Boimau(2)
Jurusan Teknik Mesin, Fakultas Sains dan Teknik, Universitas Nusa Cendana
-
Dominggus G. H. Adoe(3)
Jurusan Teknik Mesin, Fakultas Sains dan Teknik, Universitas Nusa Cendana
(*) Corresponding Author
Abstract
Abstract
The purpose of this study was to determine the effect of temperature on mechanical properties oven hybrid composite glass fiber and polyester fiber reinforce gewang leaves the fiber volume fraction (Vf) of 32%. Materials used in this study is polyester resin, glass fiber and fiber gewang leaves. Tensile test specimens were made according to ASTM standard D638 while bending test specimens made according to ASTM standard D790. The test specimen by hand lay-up method followed by suppression and left for one day. Furthermore, the composite standard tensile and bending test, then the test specimen treated with different heating. Tensile test results showed that the heat-treated specimens 1000C for one hour has a tensile strength greater than others, amounting to 62.264 MPa, while the lowest tensile strength of 28.805 MPa obtained on specimens that are subjected to 2000C for three hours. Bending test results also showed that the heat-treated specimens 1000C for one hour to have the largest bending strength which is equal to 112.340 MPa, while the lowest bending strength of 57.714 MPa obtained on specimens with heat treatment for 2000C for three hours. The results of the macro picture shows cracks in bending test specimens, whereas the tensile test specimens seen the fiber pullout, debonding and brittle fracture.
Downloads
References
Abanat J. J. D., Purnowidodo A., Irawan S.Y., 2012, “Pengaruh Fraksi Volume Serat Pelepah Gebang (Corypha Utan Lamarck) Terhadap Sifat Mekanik Pada Komposit Bermatrik Epoksi”, Jurnal Rekayasa Mesin, Vol.3, No. 2, Tahun 2012 : 352-361, ISSN 0216-468X.
Boimau K. , Dominggus G. H. A., Wenseslaus B., dan Yusak M. B., (2012), “Pengaruh Fraksi Volume Serat Terhadap Kekuatan Tarik Komposit Hybrid Berpenguat Serat Lontar Dan Serat Glass”, Seminar Nasional Sains dan Teknik 2012, Kupang.
Bukit N., dan Frida E., 2010 ,“Pengaruh Fraksi Volume Serat Ijuk Dan Serat Sabut Kelapa Sebagai Bahan Komposit Hibrid”, Jurnal Saintech, Vol. 02, No.03, September 2010, ISSN No. 2086-9681.
Carli, Widyanto S. A., Haryanto I., “Analisis Kekuatan Tarik Dan Lentur Komposit Serat Glass Jenis Woven Dengan Matriks Epoxy Dan Polyester Berlapis Simetri Dengan Metoda Manufaktur Hand Lay- Up”, TEKNIS
Vol. 7, No.1, April 2012 : 22 – 26.
Diharjo K. & Triyono T. (2000) Material Teknik, Buku Pegangan Kuliah, UNS Press, Surakarta.
Gibson, F. R. (1994). “Principle of Composite Material Mechanics”, McGraw-Hill Inc, New York.
Hull,D, “An Introduction to Composite Material”, Cambridge University Press, Cambridge, 1985.
Kaw A. K., 1997. “Mechanics of Composite Materials”, CRC Press, New York.
Lokantara I. P., Suardana N. P. G., Karohika I. M. G., Nanda, (2010), “Pengaruh Panjang Serat pada Temperatur Uji yang Berbeda Terhadap Kekuatan Tarik Komposit Polyester Serat Tapis Kelapa”, Jurnal Ilmiah Teknik Mesin Vol. 4 No.2. Oktober 2010.
Lumintang C. A. R., Soenoko R. , Wahyudi S., 2011, “Komposit Hibrid
Polyester Berpenguat Serbuk Batang dan Serat Sabut Kelapa”, Jurnal Rekayasa Mesin, Vol.2, No. 2, Tahun 2011, 145-153, ISSN 0216-468X.
Mattews, F.L. dan Rowling R.D., 1994,
Composite Material Engineering and science, Chapman and Hall, London.
Perdana M., 2013, “Pengaruh Moisture Content Dan Thermal Shock Terhadap Sifat Mekanik Dan Fisik Komposit Hibrid Berbasis Serat Gelas Dan Coir” , Jurnal Teknik Mesin Vol. 3, No. 1, April 2013 : 1-7.
Porwanto D.A., Johar L., (2008), “Karakterisasi Komposit Berpenguat Serat Bambu Dan Serat Gelas Sebagai Alternatif Bahan Baku Industri”, Jurusan Teknik Fisika FTI ITS Surabaya.
Rahman M. B.N., Kamiel B. P., (2011) , “Pengaruh Fraksi Volume Serat terhadap Sifat-sifat Tarik Komposit Diperkuat Unidirectional Serat Tebu dengan Matrik Poliester”, Jurnal Ilmiah Semesta Teknika Vol. 14, No. 2, 133-138, November 2011.
Sari N. H, Sinarep, Taufan A., Yudhyadi I., (2011), “Ketahanan Bending Komposit Hybrid Serat Batang Kelapa/Serat Gelas Dengan Matrik Urea Formaldehyde”, Jurnal Ilmiah Teknik Mesin Vol. 5 No.1. April 2011
Sitorus, J., (1996), Komposit Hibrid Serat Panjang, Serat Gelas-Ijuk Dengan Matriks Polimer, Skripsi, FMIPA USU, Medan.