ANALISIS FASA KRISTALIN PADA TULANG SAPI TIMOR DENGAN VARIASI WAKTU DAN TEMPERATUR PEMANASAN DENGAN PENGUJIAN XRD
-
raymundus rheymon soko(1*)
Teknik Mesin
-
Erich U. K. Maliwemu(2)
Universitas Nusa Cendana
-
Dominggus G. H. Adoe(3)
Universitas Nusa Cendana
(*) Corresponding Author
Abstract
The aim of this research is to identify the crystalline phase of Timor cattle bone powder and characterize it using XRD (X-Ray Diffraction) testing. This research uses a method of analyzing the results of XRD (X-Ray Diffraction) of Timor beef bones with variations in heating time and temperature. After the beef bones have been ground, the sample is oven-treated for 1 and 2 hours at a temperature of 1000C, then 5 grams of the sample is taken for testing using XRD (X-Ray Diffraction). The research results show that a 1 hour time variation at a temperature of 100 0C has a purity level of 84.07% with a diameter of 32.81 mm, and a crystallinity of 85.1%. And a time variation of 2 hours at a temperature of 1000C has a purity level of 76.68% with a diameter of 31.97 nm, and a crystallinity of 98.0%.
Downloads
References
-, I.-, -, G.-, & -, Y. Y. (2018). Karekteristik Hidroksiapatit (HA) Dari Limbah Tulang Sapi dengan Metode Mekanik-Termal. Jurnal Ilmiah Poli Rekayasa, 13(2), 43. https://doi.org/10.30630/jipr.13.2.89
Gadis Meinar Sari. (2012). Mekanisme Gangguan Remodeling Tulang Akibat Latihan Fisik Intensitas Tinggi Melalui Perubahan Kadar Glukokortikoid, Osteoprotegerin, Osteokalsin, C-Telopeptide Dan Jumlah Osteoblas Apoptotik.
Jonathan Adrianto, A. P. S. (2019). Eksperimen Dengan Media Tulang Sapi Sebagai Media Alternatif Produk Interior. Jurnal Intra, 7(2), 292–297.
Maghfury, T. I. (2020). Analisis X-Ray Diffraction (XRD) Pada Brazing Aluminium Seri 1000 Dan Stainless Steel Seri 304 Dengan Penambahan Serbuk Tembaga. 1–29.
Nugroho, A. D. (2020). Analisis X-Ray Diffraction (Xrd) Pada Brazing Antara Aluminium Seri 6061 Dengan Penambahan Filler Alusol Dan Filler Lokal.
Priyanto, D. (2017). Strategi Pengembalian Wilayah Nusa Tenggara Timur sebagai Sumber Ternak Sapi Potong. Jurnal Penelitian Dan Pengembangan Pertanian, 35(4), 167. https://doi.org/10.21082/jp3.v35n4.2016.p167-178
Sabuin, A., Boimau, K., Adoe, D. G. H., & Mesin, J. T. (2015). Pengaruh Temperatur Pengovenan terhadap Sifat Mekanik Komposit Hibrid Polyester Berpenguat Serat Glass dan Serat Daun Gewang. LONTAR Jurnal Teknik Mesin Undana (LJTMU ), 2(1), 69–78. https://ejurnal.undana.ac.id/index.php/LJTMU/article/view/490
Sapi, A. T. (2021). Amir Mukhlis 1 , Nazaruddin 2 , Giovani 3. 2(1), 33–42.
Studi, P., Fisika, P., Keguruan, F., Pendidikan, D. E. N. I., & Haluoleo, U. (2010). X-RD (X-Ray Diffractions). A1c3 06066.
Suhu, P., Waktu, D., Terhadap, K., Hidroksiapatit, K., Tulang, B., Dengan, S., Presipitasi, M., Pratama, Y., & Mesin, J. T. (2016). Mochamad Arif Irfa’i. 7–12.
Sumari, S., Prakasa, Y. F., Asrori, M. R., & Baharintasari, D. R. (2020). Analisis Kandungan Mineral Pasir Pantai Bajul Mati Kabupaten Malang Menggunakan XRF dan XRD. Fullerene Journal of Chemistry, 5(2), 58. https://doi.org/10.37033/fjc.v5i2.154
Umsb, L. (2016). MENARA Ilmu Vol. X Jilid 1 No.72 November 2016. X(72), 153–158.
Wulancahayani, E., & Rohmawati, L. (2020). ANALISIS UKURAN KRISTALIN SERBUK CaCO3/MgO HASIL KALSINASI DOLOMIT. Inovasi Fisika Indonesia, 9(2), 21–24. https://doi.org/10.26740/ifi.v9n2.p21-24
Yuliana, R., Rahim, E. A., & Hardi, J. (2017). Sintesis Hidroksiapatit Dari Tulang Sapi Dengan Metode Basah Pada Berbagai Waktu Pengadukan Dan Suhu Sintering. Kovalen, 3(3), 201. https://doi.org/10.22487/j24775398.2017.v3.i3.9329
Copyright (c) 2025 LONTAR Jurnal Teknik Mesin Undana
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.